RUSTGRIP ®
Rust and Biohazard Encapsulation
Rust and Biohazard Encapsulation
RUSTGRIP ® is a one-part polyurethane coating that combines with atmospheric moisture to cure. Upon curing, RUSTGRIP ® provides a protective coating of superior adhesion, flexibility, and abrasion/impact resistance. It is resistant to chemical solvents and acid splash. Originally designed for metal surfaces, RUSTGRIP ® demonstrates excellent adhesion to wood, concrete, fiberglass, and many other substrates.
RUSTGRIP ® is designed for the encapsulation of and adherence to tightly bonded surfaces of lead-based and other toxic paints and materials, as well as rusted surfaces. This unique ability is accomplished by the curing mechanism of the base polymer.
The coating ( having a low initial viscosity ) wets the rusty surface, then penetrates to the foundation of the rust’s origin, where curing begins. RUSTGRIP ® actually becomes part of the substrate, unlike a surface coating, which just bonds on top. The polymer literally begins to swell, developing an interlocking network between the pores of the surface and the coating. RUSTGRIP is highly recommended as a primer coat for SUPERTHERM ®. No pot life, no catalyzation, no two-part mixing.
RUSTGRIP ® is not a sacrificial rust inhibitor, such as a zinc-enriched primer that will wear out over time, but in fact a permanent rust proofing, which is why it is a certified ( ASTM E1795 ) Biohazard Encapsulator. RUSTGRIP ® has also passed 15,000 hours of salt spray testing, which far exceeds the marine specifications and consequently has achieved DNV certification. Can substitute for zinc-rich primer, requiring no white sandblasting. Can be applied over rusted surfaces after loose/flaking material is removed. High humidity quickens the dry / cure cycle.
Using RUSTGRIP ® is approximately 77% Less Expensive than a traditional 3-Part System!
Product Resources
-
Slideshow
-
RustGrip Salt Spray vs. Competition
-
Humidity Temperature Matrix
Physical Data
-
Solids: By weight 62.2% / By Volume 51.4%
-
Cure time at 70°F (21°C): 2 hours to touch. Overcoat with RUSTGRIP ® or other coatings immediately after the surface is dry to the touch to achieve proper adhesion. Higher temperatures and humidity will shorten cure times; lower temperatures will slow curing. Must be overcoated within 2 hours or within 1 hour after reaching the dry-to-touch stage, or the surface must be lightly sanded to achieve good adhesion.
-
Lead and chromate-free
-
Cures by reacting to moisture in the air
-
Weight: 9.18 lbs. per gallon
-
Surface Tensile Strength: 6,780+ psi
-
VOC Level: 3.17 lbs/gal ; 380 grams/liter
-
Impact Resistance: 200+ psi front/160+ psi back
-
Shelf Life: up to 3 years (unopened) under appropriate storage conditions (see MSDS)
Features
-
USDA approved, (safe around food) Lead & chromate free
-
Patented Biohazard Encapsulation (ASTM E1795)
-
Outstanding Adhesion (ASTM D3359) Coated over 18 coats of oil-based paint, penetrating through all 18 coats and secured to the substrate
-
6,750 psi Tensile strength equal to US highway concrete in strength
-
Performed 20,000 Window Cycling tests equal to 54 years
-
Not affected by acid splash
-
Guards against all types of corrosion
-
Was subjected to - 350°F nitrogen at Air Products Co. without effect
-
Can withstand + 325°F constant heat before the resins burn out
Limited Warranty
Unless Superior Products provides a written warranty of fitness for a particular use, Superior Products' sole warranty is that the product, as supplied, will meet the current sales specifications and is specific only to the return of the product found to be defective upon opening of the container within one year. Customer's exclusive remedy and Superior's sole liability for breach of warranty is limited to refund of the purchase price or replacement of any product shown to be other than as warranted, and Superior Products expressly disclaims any liability for incidental or consequential damage.